MC501CDR2: Conductive grade(Black)
MC501CDR6: Electro-Static Dissipative grade(Black)
MC501CDR9: Electro-Static Dissipative grade(Black)
MC500ASR11: Electro-Static Dissipative grade(Without carbon)(Ivory)
Technical parameters
Project | ASTM | Units | MC501CDR2 | MC501CDR6 | MC501CDR9 | MC500ASR11 |
Proportion | D-792 | | 1.20 | 1.23 | 1.19 | 1.15 |
Tensile strength | D-638 | Mpa | 68 | 74 | 88 | 52 |
Elongation | D-638 | % | 10 | 7 | 12 | 162 |
Tensile Modulus | D-638 | Mpa | | | | |
Compression strength (yield point) | D-695 | Mpa | | | | |
Compression strength (5% deformation) | D-695 | Mpa | 98 | 93 | | 33 |
Compression elasticity | D-695 | Mpa | 4210 | 4020 | | 1314 |
Impact test strength (notch) | D-256 | J/M | 35 | 35 | 35 | 180 |
Tortuous strength | D-790 | Mpa | 117 | 117 | 132 | 45 |
Tortuous elasticity | D-790 | Mpa | 4110 | 4020 | 4160 | 1216 |
ROCKWELL hardness | D-785 | R刻度 | 119 | 117 | 119 | 93 |
Continuous use temperature | | ℃ | 120 | 120 | 150 | 105 |
Water absorption (23 ℃, soak in water 24 hours seepage) | D-570 | % | | | | 1.6 |
Water absorption (23 ℃, the water saturation) | D-570 | % | | | | |
Coefficient of linear expansion | D-696 | X10-5/℃ | 8.0 | 7.5 | 8.6 | 11.0 |
Weight to withstand temperature | 1.820MPa (18.6kgf/cm2) | D-648 | ℃ | 200 | 200 | 200 | 75 |
0.445MPa (4.6kgf/cm2) | D-648 | ℃ | 215 | 215 | | 150 |
Volume inherent resistance | D-257 | Ω·cm | 102~104 | 106~108 | 108~1010 | 1010~1012 |
Product specifications
Sheet sizes:600(W)*1200(L)mm 500*500mm
Thickness:5,7,10,12,15,20,25,30,35,40,50mm
Bar length:1000mm,500mm,200mm
Bar diameter:10,15,20,25,30,35,40,45,50,60,70,80,90,100,110,120,130,140,150mm